Energetically modified cement
Energetically modified cements (EMC) are a class of cementitious materials made from pozzolans (e.g. fly ash, volcanic ash, pozzolana), silica sand, blast furnace slag, or Portland cement (or blends of these ingredients).[1]
Classification and field-usage potential
The term "energetically modified cement" (abbreviated as "EMC" or "EMC cement") refers to a class of cementitious materials which have been produced using a special activation process.[2][3] This process is entirely mechanical, as opposed to thermal,[3][4][5] and is carried out by finely grinding the materials to increase binding capacity.[6][7]
There are several types of energetically modified cements, depending on the raw materials used; all contain some proportion of conventional Portland cement, which may itself undergo EMC Activation, and many contain alternative (supplemental) cementitious materials. EMCs can be produced with less energy and carbon dioxide production than traditional cements.[4][8]
Each type of energetically modified cement has its own performance characteristics, including mechanical load. The most frequently used EMCs are made from fly ash and natural pozzolans; these are relatively abundant materials, and the performance characteristics are relatively close to those of Portland cement while providing energy and carbon dioxide savings. [Note 1] EMC products have been extensively tested by independent labs.[9]
History
![](../I/m/Lule%C3%A5_University_of_Technology_2011.jpg)
The term "energetically modified cement" was first used in Sweden, where the EMC Activation process was developed in 1992 by Vladimir Ronin at Luleå University of Technology (LTU). The term was introduced in a paper by Ronin et al. in 1993.[10] The process was refined by Ronin and others, including Lennart Elfgren (now Professor Emeritus of LTU).[11] Continuing academic work and research "self-healing" properties of energetically modified cements is ongoing at LTU.[12]
At the 45th World Exhibition of Invention, Research and Innovation, held in 1996 in Brussels, Belgium, EMC Activation was awarded a Gold Medal with mention by EUREKA, the European inter-governmental (research and development) organisation.[13]
The research work connected with EMCs has received awards from the Elsa ō Sven Thysells stiftelse för konstruktionsteknisk forskning (Elsa & Sven Thysell Foundation for Construction Engineering Research) of Sweden.[14]
Chemistry
Through the use of pozzolans in concrete, porous (reactive) Portlandite can be transformed into hard and impermeable (relatively non-reactive) compounds, rather than the porous and soft relatively reactive calcium carbonate produced using ordinary cement.[15] Many of the end products of pozzolanic chemistry exhibit a hardness greater than 7.0 on the Mohs scale.
EMC Activation is a process which increases a pozzolan's chemical affinity for pozzolanic reactions.[16][17] This is leads to faster and greater strength development of the resulting concrete, at higher replacement ratios, than untreated pozzolans.[18][19] These highly reactive pozzolans can yield further stabilisation benefits upon the pozzolanic reaction-pathways.
In concrete (including concretes with EMCs), Portland cement combines with water to produce a stone-like material through a complex series of chemical reactions, the full mechanics of which are still not fully understood. That chemical process, called mineral hydration, forms two cementing compounds in the concrete: calcium silicate hydrate (C-S-H) and calcium hydroxide (Ca(OH)2). This reaction can be noted in three ways, as follows:[20]
- Standard notation:
- Balanced:
- Cement chemist notation (the hyphenation denotes the variable stoichiometry): C3S + H → C-S-H + CH
The underlying hydration reaction forms two products:
- Calcium silicate hydrate (C-S-H), which gives concrete its strength and dimensional stability. The crystal structure of C-S-H in cement paste has not been fully resolved yet and there is still ongoing debate over its nanostructure.[21]
- Calcium hydroxide (Ca(OH)2), which in concrete chemistry is known also as Portlandite. In comparison to calcium silicate hydrate, Portlandite is relatively porous, permeable and soft (2 to 3, on Mohs scale).[22] It is also sectile, with flexible cleavage flakes.[23] Portlandite is soluble in water, to yield an alkaline solution which can compromise a concrete's resistance to acidic attack.[24]
Portlandite makes up about 25% of concrete made with Portland cement without pozzolanic cementitious materials.[15] In this type of concrete, carbon dioxide is slowly absorbed to convert the Portlandite into insoluble calcium carbonate (CaCO3), in a process called carbonatation:[15]
In mineral form, calcium carbonate can exhibit a wide range of hardness depending on how it is formed. At its softest, calcium carbonate can form in concrete as chalk (of hardness 1.0 on Mohs scale). Like Portlandite, calcium carbonate in mineral form can also be porous, permeable and with a poor resistance to acid attack, which causes it to release carbon dioxide.
Pozzolanic concretes, including EMCs, however, continue to consume the soft and porous Portlandite as the hydration process continues, turning it into additional hardened concrete as calcium silicate hydrate (C-S-H) rather than calcium carbonate.[15] This results in a denser, less permeable and more durable concrete.[15] This reaction is an acid-base reaction between Portlandite and silicic acid (H4SiO4) that may be represented as follows:[25]
Further, many pozzolans contain aluminiate (Al(OH)4−) that will react with Portlandite and water to form:
- calcium aluminiate hydrates, such as calcium aluminium garnet (hydrogrossular: C4AH13 or C3AH6 in cement chemist notation, hardness 7.0 to 7.5 on Mohs scale);[26] or
- in combination with silica, to form strätlingite (Ca2Al2SiO7·8H2O or C2ASH8 in cement chemist notation), which geologically can form as xenoliths in basalt as metamorphosed limestone.[27]
Pozzolanic cement chemistry (along with high-aluminiate cement chemistry) is complex and per se is not constrained by the foregoing pathways. For example, strätlingite can be formed in a number of ways, including per the following equation which can add to a concrete's strength:[28]
- C2AH8 + 2CSH + AH3 + 3H → C2ASH8 (cement chemist notation) [29]
The role of pozzolans in a concrete's chemistry is not fully understood. For example, strätlingite is metastable, which in a high temperature and water-content environment (that can be generated during the early curing stages of concrete) may of itself yield stable calcium aluminium garnet (see first bullet point above).[30] This can be represented per the following equation:
- 3C2AH8 → 2C3AH6 + AH3 + 9H (cement chemist notation) [31]
Per the first bullet point, although the inclusion of calcium aluminium garnet per se is not problematic, if it is instead produced by foregoing pathway, then micro-cracking and strength-loss can occur in the concrete.[32] However, adding high-reactivity pozzolans into the concrete mix prevents such a conversion reaction.[33] In sum, whereas pozzolans provide a number of chemical pathways to form hardened materials, "high-reactivity" pozzolans such as blast furnace slag (GGBFS) can also stabilise certain pathways. In this context, EMCs made from fly ash have been demonstrated to produce concretes that meet the same characteristics as concretes comprising "120 Slag" (i.e., GGBFS) according to U.S. standard ASTM C989.[18][34]
Portlandite, when exposed to low temperatures, moist conditions and condensation, can react with sulphate ions to cause efflorescence; pozzolanic chemistry reduces the amount of Portlandite available, to reduce efflorescence.[35] |}
Self-healing properties
Natural pozzolanic reactions can cause mortars and concretes containing these materials to "self-heal".[36][37][38] The EMC Activation process can at times increase the likelihood of the occurrence of these pozzolanic reactions.[16][17] The same tendency been noted and studied in the various supporting structures of Hagia Sophia built for the Byzantine emperor Justinian (now, Istanbul, Turkey).[39] There, in common with most Roman cements, mortars comprising high amounts of pozzolana were used — in order to give what was thought to be an increased resistance to the stress-effects caused by earthquakes.[40]
Range of characteristics
Concretes made from energetically modified cements can be designed to exhibit superior strength and durability or to exhibit rapid and ultra-rapid hardening.[41] This depends upon the "pozzolanic" characteristics of the raw material that is employed to make it. For example, fly ash in its natural state is typically, but not always, more "pozzolanic" than volcanic ash.
An important consideration in choosing a concrete material is its strength-development within a specified time period, which must match or exceed a project's specifications. According to Ronin, the current upper-limit for using EMC made from natural pozzolans is 60% for practical large-scale usage.
No noxious emissions and low leachability of EMCs
The EMC activation of fly ash is a mechanical process, and does not involve heating or burning.[8] Leachability tests were performed by LTU in 2001 in Sweden on behalf of a Swedish power production company. These tests confirmed that EMC made from fly ash "showed a low surface specific leachability" with respect to "all environmentally relevant metals." [42][43]
EMCs using California volcanic ash
![](../I/m/EMC_Cement_Natural_Pozzolan_Deposits_(Southern_California).jpg)
Energetically modified cements have been used in large infrastructure projects in the United States.> EMCs made by replacing at least 50% of the Portland cement with have yielded consistent field results in high-volume applications.[18] This is also the case for EMC made from natural pozzolans (e.g., volcanic ash).[19]
Volcanic ash deposits from Southern California were independently tested; at 50% Portland cement replacement, the resulting concretes exceeded requirements.[44] At 28 days, the compressive strength was 4,180 psi / 28.8 MPa (N/mm²). The 56-day strength exceeded the requirements for 4,500 psi (31.1 MPa) concrete, even taking into account the safety margin as recommended by the American Concrete Institute.[45] The concrete made in this way was workable and sufficiently strong, exceeding the 75% standard of pozzolanic activity at both 7 days and 28 days.[44] The surface smoothness of pozzolans in the concrete was also increased.[44]
Durability of concretes produced and high-performance concretes (HPCs)
Treating Portland cement with EMC activation will yield high-performance concretes. These HPCs will be high strength, highly durable, and exhibiting greater strength-development in contrast to HPCs made from untreated Portland cement. Concrete made from ordinary Portland cement without additives has a relatively impaired resistance to salt waters.[46] Treating Portland cement with the EMC activation process may increase the strength development by nearly 50% and also significantly improve the durability, as measured according to generally accepted methods.[46]
Energetically modified cements also exhibit high resistances to chloride and sulphate ion attack, together with low alkali-silica reactivities (ASR).[18] Like all concretes comprising pozzolans, they are more durable than concretes made from Portland cement.[24]
Projects using EMC
An early project using EMC made from fly ash was the construction of a road bridge in Karungi, Sweden, with Swedish construction firm Skanska. The Karungi road bridge has withstood Karungi's harsh subarctic climate and divergent annual and diurnal temperature ranges.[8]
![](../I/m/EMC_Cement_(CemPozz)_IH-10_Texas.jpg)
In the United States, energetically modified cements have been approved for usage by a number of state transportation agencies, including PennDOT, TxDOT and CalTrans.[9]
In the United States, highway bridges and hundreds of miles of highway paving have been constructed using concretes made from EMC derived from fly ash. These projects include sections of Interstate 10. In these projects, EMC replaced at least 50% of the Portland cement in the concrete poured.[18] This is about 2.5 times more than the typical amount of fly ash in projects where energetic modification is not used.[47] Independent text data showed acceptable 28-day strength requirements in all projects.[18]
Another project was the extension of the passenger terminals at the Port of Houston, Texas, where energetically modified cement's ability to yield concretes that exhibit high resistances to chloride– and sulphate–ion permeability (i.e., increased resistance to sea waters) was a factor.
Production
EMCs have been in production since 1992. As of 2010 the volume of concrete produced containing a least partially energetically modified cement was about 4,500,000 cu yd (3,440,496 m3). This represents approximately 0.13% of the yearly worldwide concrete production.[48]
See also
Background science to EMC Activation:
- Archard equation
- Asperity
- Contact mechanics
- Crystallinity
- Crystal structure
- Fretting
- Frictional contact mechanics
- Galling
- Hardness
- Lattice constant
- Material mechanics
- Materials science
- Microstructure
- Nanotribology
- Peter Adolf Thiessen
- Surface engineering
- Surface metrology
- Tribology
- X-ray crystallography
- X-ray fluorescence (XRF)
Academic:
Notes
- ↑ Two aspects: (I) 2011 Global Portland cement production was approximately 3.6 million tonnes per United States Geological Survey (USGS) (2013) data, and is binding as a reasonably accurate assimilation, rather than an estimate per se. Note also, that by the same report, for 2012 it is estimated that Global Portland cement production increased to 3.7 billion tonnes (a 100 million tonne increase, year-on-year). (II) 2011 Estimate of Global total CO2 production: 33.376 billion tonnes (without international transport). Source: E.U. European Commission, Joint Research Centre (JRC)/PBL Netherlands Environmental Assessment Agency. Emission Database for Global Atmospheric Research (EDGAR), release version 4.2. The 2009–2011 trends were estimated for energy-related sectors based on fossil fuel consumption for 2009–2011 from the BP Review of World Energy 2011 (BP, 2012), for cement production based on preliminary data from USGS (2012), except for China for which use was made of National Bureau of Statistics of China (NBS) (2009, 2010, 2011). [As of May 2013. See, EDGAR, external link section].
- ↑ Further notes on pozzolanic chemistry: (A) The ratio Ca/Si (or C/S) and the number of water molecules can vary, to vary C-S-H stoichiometry. (B) Often, crystalline hydrates are formed for example when tricalcium aluminiate reacts with dissolved calcium sulphate to form crystalline hydrates (3CaO·(Al,Fe)2O3·CaSO4·nH2O, general simplified formula). This is called an AFm ("alumina, ferric oxide, monosulphate") phase. (C) The AFm phase per se is not exclusive. On the one hand while sulphates, together with other anions such as carbonates or chlorides can add to the AFm phase, they can also cause an AFt phase where ettringite is formed (6CaO·Al2O3·3SO3·32H2O or C6S3H32). (D) Generally, the AFm phase is important in the further hydration process, whereas the AFt phase can be the cause of concrete failure known as DEF. DEF can be a particular problem in non-pozzolanic concretes (see, for ex., Folliard, K., et al., Preventing ASR/DEF in New Concrete: Final Report, TXDOT & U.S. FHWA:Doc. FHWA/TX-06/0-4085-5, Rev. 06/2006). (E) It is thought that pozzolanic chemical pathways utilising Ca2+ ions cause the AFt route to be relatively suppressed.
References
- ↑ Mark Anthony Benvenuto (24 February 2015). Industrial Chemistry: For Advanced Students. De Gruyter. pp. 134–. ISBN 978-3-11-035170-5.
- ↑ Humpreys, K.; Mahasenan, M. (2002). Toward a Sustainable Cement Industry Substudy 8: Climate Change. Geneva, Swtizerland: World Business Council for Sustainable Development (WBCSD).
- 1 2 Harvey, D (2013). Energy and the New Reality 1 – Energy Efficiency and the Demand for Energy Services. Taylor & Francis. ISBN 9781136542718.
- 1 2 Kumar, R; Kumar, S; Mehrotra, S (2007). "Towards sustainable solutions for fly ash through mechanical Activation". Resources Conservation and Recycling. London: Elsevier Ltd. 52 (2): 157–179. doi:10.1016/j.resconrec.2007.06.007. ISSN 0921-3449.
- ↑ Hasanbeigi, A; Price, L; Lin, E; Lawrence Berkeley National Laboratory, LBNL Paper LBNL-5434E (2013). "Emerging Energy-efficiency and CO2 Emission-reduction Technologies for Cement and Concrete Production". Renewable and Sustainable Energy Reviews. London: Elsevier Ltd. 16 (8): 6220–6238. doi:10.1016/j.rser.2012.07.019. ISSN 1364-0321.
- ↑ Danny Harvey (12 August 2010). Energy and the New Reality 1 - Energy Efficiency and the Demand for Energy Services. Routledge. pp. 385–. ISBN 1-136-54272-8.
- ↑ Jean-Pierre Bournazel; Yves Malier (1998). PRO 4: International RILEM Conference on Concrete: From Material to Structure. RILEM Publications. pp. 101–. ISBN 978-2-912143-04-4.
- 1 2 3 Hedlund, H; Ronin, V; Jonasson, J-E; Elfgren, L (1999). "Grönare Betong" [Green Cement]. 91 (7). Stockholm, Sweden: Förlags AB Bygg & teknik: 12–13.
- 1 2 United States Federal Highway Administration (FHWA). "EMC Cement Presentation January 18, 2011". Washington, DC.
- ↑ Ronin, V.; Jonasson, J.E. (1993). "New concrete technology with the use of energetically modified cement (EMC)". Proceedings: Nordic Concrete Research Meeting, Göteborg, Sweden. Oslo, Norway: Norsk Betongforening (Nordic concrete research): 53–55.
- ↑ LTU website. "Professor Lennart Elfgren". ltu.se.
- ↑ Eflgren, L.; Future Infrastructure Forum, Cambridge University (28 March 2013). "Future Infrastructure Forum: Scandinavian Points of View".
- ↑ EUREKA. "EUREKA Gold Award for EMC Cement" (PDF).
- ↑ "Stipendieutdelning" (in Swedish). Luleå tekniska universitet. Retrieved 24 March 2014.
- 1 2 3 4 5 Baroghel Bouny, V (1996). Bournazel, J. P.; Malier, Y., eds. Texture and Moisture Properties of Ordinary and High Performance Cementitious Materials (in PRO 4: Concrete: From Material to Structure). 144 at 156: RILEM. p. 360. ISBN 2-912143-04-7.
- 1 2 Justnes, H; Elfgren, L; Ronin, V (2005). "Mechanism for performance of energetically modified cement versus corresponding blended cement". Cement and Concrete Research. Elsevier (London) and Pergamon Press (Oxford). 35 (2): 315–323. doi:10.1016/j.cemconres.2004.05.022. ISSN 0008-8846.
- 1 2 Patent abstract for granted patent "Process for Producing Blended Cements with Reduced Carbon Dioxide Emissions" (Pub. No.:WO/2004/041746; International Application No.: PCT/SE2003001009; Pub. Date: 21.05.2004; International Filing Date: 16.06.2003)
- 1 2 3 4 5 6 EMC Cement BV. Summary of CemPozz® (Fly Ash) Performance in Concrete (PDF). EMC Cement BV, 2012.
- 1 2 EMC Cement BV. Summary of CemPozz® (Natural Pozzolan) Performance in Concrete (PDF). EMC Cement BV, 2012.
- ↑ "Cement hydration". Understanding Cement.
- ↑ See, for ex., Thomas, Jeffrey J.; Jennings, Hamlin M. (January 2006). "A colloidal interpretation of chemical aging of the C-S-H gel and its effects on the properties of cement paste". Cement and Concrete Research. Elsevier. 36 (1): 30–38. doi:10.1016/j.cemconres.2004.10.022. ISSN 0008-8846.
- ↑ Portlandite at Webmineral
- ↑ Handbook of Mineralogy
- 1 2 Chappex, T.; Scrivener K. (2012). "Alkali fixation of C-S-H in blended cement pastes and its relation to alkali silica reaction". Cement and Concrete Research. 42 (8): 1049–1054. doi:10.1016/j.cemconres.2012.03.010.
- ↑ Mertens, G.; Snellings, R.; Van Balen, K.; Bicer-Simsir, B.; Verlooy, P.; Elsen, J. (March 2009). "Pozzolanic reactions of common natural zeolites with lime and parameters affecting their reactivity". Cement and Concrete Research. 39 (3): 233–240. doi:10.1016/j.cemconres.2008.11.008.
- ↑ Ca3Al2(SiO4)3−x(OH)4x, with hydroxide (OH) partially replacing silica (SiO4)
- ↑ Webmineral.com. "Stratlingite Mineral Data". Retrieved 6 December 2013. . See, also, Ding, Jian; Fu, Yan; Beaudoin, J.J. (August 1995). "Strätlingite formation in high alumina cement – silica fume systems: Significance of sodium ions". Cement and Concrete Research. 25 (6): 1311–1319. doi:10.1016/0008-8846(95)00124-U.
- ↑ Midgley, H.G.; Bhaskara Rao, P. (March 1978). "Formation of stratlingite, 2CaO.SiO2.Al2O3.8H2O, in relation to the hydration of high alumina cement". Cement and Concrete Research. 8 (2): 169–172. doi:10.1016/0008-8846(78)90005-4. ISSN 0008-8846. . See, also, Midgley, H.G. (March 1976). "Quantitative determination of phases in high alumina cement clinkers by X-ray diffraction". Cement and Concrete Research. 6 (2): 217–223. doi:10.1016/0008-8846(76)90119-8. ISSN 0008-8846.
- ↑ Heikal, M.; Radwan, M M; Morsy, M S (2004). "Influence of curing temperature on the Physico-mechanical, Characteristics of Calcium Aluminate Cement with air cooled Slag or water cooled Slag" (PDF). Ceramics-Silikáty. 48 (4): 185–196. . See, also, Abd-El.Aziz, M.A.; Abd.El.Aleem, S.; Heikal, Mohamed (January 2012). "Physico-chemical and mechanical characteristics of pozzolanic cement pastes and mortars hydrated at different curing temperatures". Construction and Building Materials. 26 (1): 310–316. doi:10.1016/j.conbuildmat.2011.06.026. ISSN 0950-0618.
- ↑ Mostafa, Nasser Y.; Zaki, Z.I.; Abd Elkader, Omar H. (November 2012). "Chemical activation of calcium aluminate cement composites cured at elevated temperature". Cement and Concrete Composites. 34 (10): 1187–1193. doi:10.1016/j.cemconcomp.2012.08.002. ISSN 0958-9465.
- ↑ Taylor, HFW, (1990) Cement chemistry, London: Academic Press, pp.319–23.
- ↑ Matusinović, T; Šipušić, J; Vrbos, N (November 2003). "Porosity–strength relation in calcium aluminate cement pastes". Cement and Concrete Research. 33 (11): 1801–1806. doi:10.1016/S0008-8846(03)00201-1. ISSN 0008-8846.
- ↑ See, for ex., Majumdar, A.J.; Singh, B. (November 1992). "Properties of some blended high-alumina cements". Cement and Concrete Research. 22 (6): 1101–1114. doi:10.1016/0008-8846(92)90040-3. ISSN 0008-8846.
- ↑ ASTM International (2010). "ASTM C989: Standard Specification for Slag Cement for Use in Concrete and Mortars". Book of Standards Volume. 4.02. doi:10.1520/c0989-10.
- ↑ Nhar, H.; Watanabe, T.; Hashimoto, C. & Nagao, S. (2007). Efflorescence of Concrete Products for Interlocking Block Pavements (Ninth CANMET/ACI International Conference on Recent Advances in Concrete Technology: Editor, Malhotra, V., M., 1st ed.). Farmington Hills, Mich.: American Concrete Institute. pp. 19–34. ISBN 9780870312359.
- ↑ Yang, Y; Lepech, M. D.; Yang, E.; Li, V. C. (2009). "Autogenous healing of engineered cementitious composites under wet-dry cycles". Cement and Concrete Research. 39 (5): 382–390. doi:10.1016/j.cemconres.2009.01.013. ISSN 0008-8846.
- ↑ Li, V., C.; Herbert, E., (2012). "Robust Self-Healing Concrete for Sustainable Infrastructure". Journal of Advanced Concrete Technology. Japan Concrete Institute. 10 (6): 207–218. doi:10.3151/jact.10.207.
- ↑ Van Tittelboom, K.; De Belie, N. (2013). "Self-Healing in Cementitious Materials—A Review". Materials. 6 (6): 2182–2217. Bibcode:2013Mate....6.2182V. doi:10.3390/ma6062182. ISSN 1996-1944.
- ↑ Moropoulou, A.; Cakmak, A.; Labropoulos, K.C.; Van Grieken, R.; Torfs, K. (January 2004). "Accelerated microstructural evolution of a calcium-silicate-hydrate (C-S-H) phase in pozzolanic pastes using fine siliceous sources: Comparison with historic pozzolanic mortars". Cement and Concrete Research. 34 (1): 1–6. doi:10.1016/S0008-8846(03)00187-X.
- ↑ Moropoulou, A; Cakmak, A., S., Biscontin, G., Bakolas, A., Zendri, E.; Biscontin, G.; Bakolas, A.; Zendri, E. (December 2002). "Advanced Byzantine cement based composites resisting earthquake stresses: the crushed brick/lime mortars of Justinian's Hagia Sophia". Construction and Building Materials. 16 (8): 543. doi:10.1016/S0950-0618(02)00005-3. ISSN 0950-0618.
- ↑ United States Federal Highway Administration (FHWA). What is High Performance Concrete. Washington, DC.
- ↑ Private study, Luleå University of Technology (2001) "Diffusionstest för cementstabiliserad flygaska", LTU Rapport AT0134:01, 2001-09-03
- ↑ Ronin, V; Jonasson, J-E; Hedlund, H (1999). "Ecologically effective performance Portland cement-based binders", proceedings in Sandefjord, Norway 20–24 June 1999. Norway: Norsk Betongforening. pp. 1144–1153.
- 1 2 3 Stein, B (2012). A Summary of Technical Evaluations & Analytical Studies of Cempozz® Derived from Californian Natural Pozzolans (PDF). San Francisco, United States: Construction Materials Technology Research Associates, LLC.
- ↑ ACI 318 "Building Code Requirements for Structural Concrete and Commentary"
- 1 2 Bache, M (1983). "Densified cement/ultra fine particle-based materials". Proceedings of the Second International Conference on Superplasticizers in Concrete.
- ↑ Schneider, M.; Romer M., Tschudin M. Bolio C.; Tschudin, M.; Bolio, H. (2011). "Sustainable cement production – present and future". Cement and Concrete Research. 41 (7): 642–650. doi:10.1016/j.cemconres.2011.03.019.
- ↑ "Text of H.Res. 394 (108th): Recognizing the American Concrete Institute's 100-year contribution as the standards development organization of ... (Passed the House (Engrossed) version)". GovTrack.us. 2003-11-04. Retrieved 2014-03-26.
External links
- Official website for EMC Cement, Sweden – at EMCcement.com
- Luleå University of Technology, Sweden – at LTU.se
- Future Infrastructure Forum, University of Cambridge, United Kingdom – at Fif.construction.cam.ac.uk
- U.S. Geological Survey (USGS) Cement Statistics and Information – at Minerals.usgs.gov
- U.S. Environmental Protection Agency (EPA), Rule Information for Portland Cement Industry – at EPA.gov
- American Concrete Institute – at Concrete.org
- EDGAR – Emission Database for Global Atmospheric Research – at Edgar.jrc.ec.europa.eu
- Vitruvious: The Ten Books on Architecture online: cross-linked Latin text and English translation
- WBCSD Cement Sustainability Initiative – at Wbcsdcement.org