Uddeholms AB

This type of production has three phases. First, steel scrap is melted in an Electric Arc Furnace. After melting, the steel is purified in a secondary metallurgical treatment to remove sulfur, slag and other unwanted materials. In the third step, the steel is poured into an ingot. Different methods such as Up-hill casting and the use of protective noble gases can improve purity further.

In the electro-slag remelting (ESR) process, steel scrap is first melted using the conventional process but is then remelted in a water-cooled form. With this process, a more even microstructure can be achieved which gives completely different properties than a material produced with the conventional method. There are different variants of the electro-slag remelting process where the remelting is done in vacuum or a protective atmosphere.

Production process for powder metallurgical capsules.

In the powder metallurgical process, a fine powder is created by spraying a stream of liquid steel with nitrogen under high pressure. The average diameter of the powder is 50-100 µm. The powder is filled into capsules directly in order to avoid contamination. With hot isostatic pressing (HIP), the powder is consolidated to 100% density. The advantage with powder metallurgical tool steels is to have a high degree of alloys without getting segregations in the material. This makes it possible to combine high material hardness with wear resistance.

The GRANSHOT process was developed at UDDEHOLM. In the GRANSHOT process, hot liquid molten metal is poured at a flat surface, dispersing it so that small droplets are created. These metal droplets are immediately cooled in water, creating granules which are dewatered. The process is applicable to iron, steel, stainless steel, ferro alloys and base metals. These granules have ideal metallurgical and logistical properties as to facilitate the use of granules into blast furnaces, electric arc furnaces, AODs, foundries etc. For example, the granules can be used in casting of tools in order to achieve tools with even metallurgical properties. In 2007, the independent and privately owned Swedish engineering company UHT - Uvån Hagfors Teknologi AB, was formed and also took over all intellectual property rights including the trademark GRANSHOT. UDDEHOLM has continued to produce metal granulates, so called Granshots, using their GRANSHOT unit in Hagfors, Sweden.

Cold Work Steels are tool steels used for tools where the work material is cold. The steel is exposed to mechanical forces by the work material. Common problems are wear, chipping, plastic deformation and cracking which can lead to tool failure. Application areas are stamping, deep drawing, cold extrusion, fine blanking, cold forging, form pressing and rolling.

Hot Work Steels are tool steels that are used for tools where the material is hot. Due to the high temperatures when working with molten metals such as aluminium, iron and brass, the requirements on the tools are very high. High heat resistance and ductility as well as wear resistance are important. Resistance to thermal cyclic stress is also good. Application areas are casting, extrusion and forging.

Plastic Mold Steels are tool steels used for production of plastic parts. The most important characteristics are durability and hardness, toughness, wear resistance, polishability, corrosion resistance, and thermal heat conductivity. Important customer groups are in the automotive, consumer goods industry, electronics and other industries that use plastic components. Application areas are blow molding, form pressing, form blowing, extrusion and holder materials.

Mechanical components such as engine parts (shafts cog wheels), machine parts, wear parts can be made of tool steel. The combinations of hardness, toughness, corrosion resistance and other properties of tool steels, makes it possible to replace more traditional engineering steels.