Rockwell scale

The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measuring the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load).[1] There are different scales, denoted by a single letter, that use different loads or indenters. The result is a dimensionless number noted as HRA, HRB, HRC, etc., where the last letter is the respective Rockwell scale (see below). When testing metals, indentation hardness correlates linearly with tensile strength.[2]

A Rockwell hardness tester

History

The differential depth hardness measurement was conceived in 1908 by a Viennese professor Paul Ludwik in his book Die Kegelprobe (crudely, "the cone test").[3] The differential-depth method subtracted out the errors associated with the mechanical imperfections of the system, such as backlash and surface imperfections. The Brinell hardness test, invented in Sweden, was developed earlier – in 1900 – but it was slow, not useful on fully hardened steel, and left too large an impression to be considered nondestructive.

Hugh M. Rockwell (1890–1957) and Stanley P. Rockwell (1886–1940) from Connecticut in the United States co-invented the "Rockwell hardness tester," a differential-depth machine. They applied for a patent on July 15, 1914.[4] The requirement for this tester was to quickly determine the effects of heat treatment on steel bearing races. The application was subsequently approved on February 11, 1919, and holds U.S. Patent 1,294,171. At the time of invention, both Hugh and Stanley Rockwell worked for the New Departure Manufacturing Co. of Bristol, CT.[5] New Departure was a major ball bearing manufacturer which in 1916 became part of United Motors and, shortly thereafter, General Motors Corp.

After leaving the Connecticut company, Stanley Rockwell, then in Syracuse, NY, applied for an improvement to the original invention on September 11, 1919, which was approved on November 18, 1924. The new tester holds U.S. Patent 1,516,207.[6][7] Rockwell moved to West Hartford, CT, and made an additional improvement in 1921.[7] Stanley collaborated with instrument manufacturer Charles H. Wilson of the Wilson-Mauelen Company in 1920 to commercialize his invention and develop standardized testing machines.[8] Stanley started a heat-treating firm circa 1923, the Stanley P. Rockwell Company, which still exists in Hartford, CT. The later-named Wilson Mechanical Instrument Company has changed ownership over the years, and was acquired by Instron Corp. in 1993.[9]

Rockwell hardness tester classifications based on Rockwell scales

Rockwell hardness tester: HRA, HRB, HRC [10]

Superficial Rockwell hardness tester: 15N, 30N, 45N, 15T, 30T, 45T, 15W, 30W, 45W, 15X, 30X, 45X, 15Y, 30Y, 45Y

Plastic Rockwell hardness tester: HRE, HRL, HRM

Twin Rockwell hardness tester (also named as Rockwell & superficial Rockwell hardness tester): HRA, HRB, HRC,15N, 15T, 15W, 15X, 15Y, 30N, 30T, 30W, 30X, 30Y, 45N, 45T, 45W, 45X, 45Y [11]

Operation
Force diagram of Rockwell test
A closeup of the indenter and anvil on a Rockwell-type hardness tester.
A digital Rockwell tester

The determination of the Rockwell hardness of a material involves the application of a minor load followed by a major load. The minor load establishes the zero position. The major load is applied, then removed while still maintaining the minor load. The depth of penetration from the zero datum is measured from a dial, on which a harder material gives a higher number. That is, the penetration depth and hardness are inversely proportional. The chief advantage of Rockwell hardness is its ability to display hardness values directly, thus obviating tedious calculations involved in other hardness measurement techniques.

The equation for Rockwell Hardness is , where d is the depth (from the zero load point), and N and s are scale factors that depend on the scale of the test being used (see following section).

It is typically used in engineering and metallurgy. Its commercial popularity arises from its speed, reliability, robustness, resolution and small area of indentation.

Legacy Rockwell hardness testers operation steps:

  1. Load an initial force: Rockwell hardness test initial test force is 10 kgf (98 N; 22 lbf); superficial Rockwell hardness test initial test force is 3 kgf (29 N; 6.6 lbf).
  2. Load main load: reference below form / table 'Scales and values'.
  3. Leave the main load for a "dwell time" sufficient for indentation to come to a halt.
  4. Release load; the Rockwell value will typically display on a dial or screen automatically.[12]

In order to get a reliable reading the thickness of the test-piece should be at least 10 times the depth of the indentation.[13] Also, readings should be taken from a flat perpendicular surface, because convex surfaces give lower readings. A correction factor can be used if the hardness of a convex surface is to be measured.[14]

Scales and values

There are several alternative scales, the most commonly used being the "B" and "C" scales. Both express hardness as an arbitrary dimensionless number.

Various Rockwell scales[15]
ScaleAbbreviationLoadIndenterUse N s
AHRA60 kgf120° diamond spheroconical†Tungsten carbide 100 0.002mm
BHRB100 kgf1⁄16-inch-diameter (1.588 mm) steel sphereAluminium, brass, and soft steels 130 0.002mm
CHRC150 kgf120° diamond spheroconicalHarder steels >B100 100 0.002mm
DHRD100 kgf120° diamond spheroconical 100 0.002mm
EHRE100 kgf1⁄8-inch-diameter (3.175 mm) steel sphere 130 0.002mm
FHRF60 kgf1⁄16-inch-diameter (1.588 mm) steel sphere 130 0.002mm
GHRG150 kgf1⁄16-inch-diameter (1.588 mm) steel sphere 130 0.002mm
HHRH60 kgf1⁄8-inch-diameter (3.175 mm) steel sphereAluminum, Zinc, Lead [16]
KHRK150 kgf1⁄8-inch-diameter (3.175 mm) steel sphereBearing alloy, tin, hard plastic materials [17]
†Also called a brale indenter
  • Except for testing thin materials in accordance with A623, the steel indenter balls have been replaced by tungsten carbide balls of the varying diameters. When a ball indenter is used, the letter "W" is used to indicate a tungsten carbide ball was used, and the letter "S" indicates the use of a steel ball. E.g.: 70 HRBW indicates the reading was 70 in the Rockwell B scale using a tungsten carbide indenter.[18]

The superficial Rockwell scales use lower loads and shallower impressions on brittle and very thin materials. The 45N scale employs a 45-kgf load on a diamond cone-shaped Brale indenter, and can be used on dense ceramics. The 15T scale employs a 15-kgf load on a 1⁄16-inch-diameter (1.588 mm) hardened steel ball, and can be used on sheet metal.

The B and C scales overlap, such that readings below HRC 20 and those above HRB 100, generally considered unreliable, need not be taken or specified.

Typical values
  • Very hard steel (e.g. chisels, quality knife blades): HRC 55–66 (Hardened High Speed Carbon and Tool Steels such as M2, W2, O1, CPM-M4, and D2, as well as many of the newer powder metallurgy Stainless Steels such as S30V, CPMS-154, ZDP-189, etc.)[19]
  • Axes: about HRC 45–55
  • Brass: HRB 55 (Low brass, UNS C24000, H01 Temper) to HRB 93 (Cartridge Brass, UNS C26000 (260 Brass), H10 Temper)[20]

Several other scales, including the extensive A-scale, are used for specialized applications. There are special scales for measuring case-hardened specimens.

Standards
  • International (ISO)
    • ISO 6508-1: Metallic materials—Rockwell hardness test—Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T)
    • ISO 6508-2: Metallic materials—Rockwell hardness test—Part 2: Verification and calibration of testing machines and indenters
    • ISO 6508-3: Metallic materials—Rockwell hardness test—Part 3: Calibration of reference blocks
    • ISO 2039-2: Plastics—Determination of hardness—Part 2: Rockwell hardness
  • US standard (ASTM International)
    • ASTM E18: Standard methods for Rockwell hardness and Rockwell superficial hardness of metallic materials

See also

References
  1. E.L. Tobolski & A. Fee, "Macroindentation Hardness Testing," ASM Handbook, Volume 8: Mechanical Testing and Evaluation, ASM International, 2000, pp. 203–211, ISBN 0-87170-389-0.
  2. "Correlation of Yield Strength and Tensile Strength with Hardness for Steels", E. J. Pavlina and C. J. Van Tyne, Journal of Materials Engineering and Performance, Volume 17, Number 6 / December 2008
  3. G.L. Kehl, The Principles of Metallographic Laboratory Practice, 3rd Ed., McGraw-Hill Book Co., 1949, p. 229.
  4. H.M. Rockwell & S.P. Rockwell, "Hardness-Tester," U.S. Patent 1,294,171, Feb 1919.
  5. S.W. Kallee: Stanley Pickett Rockwell - One of the Inventors of the Rockwell Hardness Testing Machine. Retrieved on 21 November 2018.
  6. S.P. Rockwell, "The Testing of Metals for Hardness, Transactions of the American Society for Steel Treating, Vol. II, No. 11, August 1922, pp. 1013–1033.
  7. S. P. Rockwell, "Hardness-Testing Machine", U.S. Patent 1,516,207, Nov 1924.
  8. V.E. Lysaght, Indentation Hardness Testing, Reinhold Publishing Corp., 1949, pp. 57–62.
  9. R.E. Chinn, "Hardness, Bearings, and the Rockwells," Advanced Materials & Processes, Vol 167 #10, October 2009, p 29-31.
  10. EBP R-150T digital Rockwell hardness tester http://www.hiebp.com
  11. EBP RSR-45/150D digital Rockwell & superficial Rockwell hardness tester http://www.hiebp.com
  12. http://www.hiebp.com
  13. Fundamentals of Rockwell Hardness Testing, archived from the original on 2010-01-29, retrieved 2010-09-10
  14. PMPA's Designer's Guide: Heat treatment, archived from the original on 2009-07-14, retrieved 2009-06-19.
  15. Smith, William F.; Hashemi, Javad (2001), Foundations of Material Science and Engineering (4th ed.), McGraw-Hill, p. 229, ISBN 0-07-295358-6
  16. EBP company R-150T Rockwell hardness tester manual book.
  17. EBP company R-150T Rockwell hardness tester manual book.
  18. E18-08b Section 5.1.2.1 & 5.2.3
  19. Knife blade materials
  20. matweb.com, accessed 2010-06-23
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.