Corundum

Corundum from Brazil, size about 2 cm × 3 cm (0.8 in × 1 in).

Corundum occurs as a mineral in mica schist, gneiss, and some marbles in metamorphic terranes. It also occurs in low-silica igneous syenite and nepheline syenite intrusives. Other occurrences are as masses adjacent to ultramafic intrusives, associated with lamprophyre dikes and as large crystals in pegmatites.[5] It commonly occurs as a detrital mineral in stream and beach sands because of its hardness and resistance to weathering.[5] The largest documented single crystal of corundum measured about 65 cm × 40 cm × 40 cm (26 in × 16 in × 16 in), and weighed 152 kg (335 lb).[9] The record has since been surpassed by certain synthetic boules.[10]

Corundum for abrasives is mined in Zimbabwe, Pakistan, Afghanistan, Russia, Sri Lanka, and India. Historically it was mined from deposits associated with dunites in North Carolina, US and from a nepheline syenite in Craigmont, Ontario.[5] Emery-grade corundum is found on the Greek island of Naxos and near Peekskill, New York, US. Abrasive corundum is synthetically manufactured from bauxite.[5]

Four corundum axes dating back to 2500 BCE from the Liangzhou culture have been discovered in China.[11]

• In 1837, Marc Antoine Gaudin made the first synthetic rubies by reacting alumina at a high temperature with a small amount of chromium as a pigment.[12]
• In 1847, J.J. Ebelmen made white synthetic sapphires by reacting alumina in boric acid.
• In 1877 Frenic and Freil made crystal corundum from which small stones could be cut. Frimy and Auguste Verneuil manufactured artificial ruby by fusing BaF
  ₂ and Al
  ₂O
  ₃ with a little chromium at temperatures above 2,000 °C (3,630 °F).
• In 1903, Verneuil announced that he could produce synthetic rubies on a commercial scale using this flame fusion process.[13]

The Verneuil process allows the production of flawless single-crystal sapphire and ruby gems of much larger size than normally found in nature. It is also possible to grow gem-quality synthetic corundum by flux-growth and hydrothermal synthesis. Because of the simplicity of the methods involved in corundum synthesis, large quantities of these crystals have become available on the market causing a significant reduction of price in recent years.

Apart from ornamental uses, synthetic corundum is also used to produce mechanical parts (tubes, rods, bearings, and other machined parts), scratch-resistant optics, scratch-resistant watch crystals, instrument windows for satellites and spacecraft (because of its transparency in the ultraviolet to infrared range), and laser components. For example, the KAGRA gravitational wave detector's main mirrors are 23 kg (50 lb) sapphires,[14] and Advanced LIGO considered 40 kg (88 lb) sapphire mirrors.[15]

Crystal structure of corundum

Molar volume vs. pressure at room temperature.

Corundum crystallizes with trigonal symmetry in the space group R3c and has the lattice parameters a = 4.75 Å and c = 12.982 Å at standard conditions. The unit cell contains six formula units.

The toughness of corundum is sensitive to surface roughness[16][17] and crystallographic orientation.[18] It may be 6–7 MPa·m^½ for synthetic crystals,[18] and around 4 MPa·m^½ for natural.[19]

In the lattice of corundum, the oxygen atoms form a slightly distorted hexagonal close packing, in which two-thirds of the gaps between the octahedra are occupied by aluminium ions.

Wikimedia Commons has media related to Corundum.

• aluminium oxide
• Gemstone
• Ruby – red corundum
• Sapphire – bluish corundum
• Spinel – natural & synthetic mineral often mistaken for corundum
• Verneuil process